EVENTS

HX-P-5818/HX-I-5311

1、特性:低密度,中硬度。

Characteristic:Low density,Medium hardness.

2、用途:用于休闲鞋、连帮鞋鞋底的生产。

Applications:For casual shoes and direct injection shoes.

3、原液特性:

Typicalproperties of PU resin:

品名

Name of products

外观

Appearance

粘度

Viscosity

(mPa.s/40℃)

密度

Density

(g/cm3/40℃)

包装

Package

(kg)

HX-P-5818

液状或蜡状

Liquid  or waxy

2300-2500

1.16-1.19

18(Net)

绿标签green  label

HX-I-5311

透明液体无异物

Transparent  and pure liquid

450-650

1.18-1.20

20(Net)

红标签red  label

4、催化剂与辅助剂 catalyst and adjuvant

催化剂/18kg  catalyst/18kg

水/18kg  water/18kg

硬化剂/18kg  hardner/18kg

根据需要添加350-400g

Add  350-400g according to the reality

根据需要添加60-90g

Add  60-90g according to the reality

根据需要添加0-300g

Add  0-300g according to the reality

5、原料预热 Materials preheat

HX-P-5818

HX-I-5311

催化剂C-3

50-60℃预热6-8小时

Preheated at 50-60℃ for 6-8 hours

50-60℃预热6-8小时

Preheated at 50-60℃ for 6-8 hours

无需加热

Without heating

6、成型条件及反应参数 Typical processing parameters & Reaction parameter

项目

Items

使用温度

Materials Temperatures

混合比

Mix ratio

(By weight)

自由泡密度

Free rise foam density(g/cm3)

成品密度

Product density(g/cm3)

模具温度

Mold temperature(℃)

脱模时间

Demold time(min)

参数

parameter

46-48/42-45

100/89-91

0.22-0.30

0.45-0.60

50-60

4-6

7、制品物性值 Physical properties

项目

Items

硬度

Hardness

(ShoreA)

拉伸强度

Tensile strength

(Mpa)

伸长率

Elongation

(%)

撕裂强度

Tear strength

(KN/m)

耐折

Ross Flexing

室温room temperature

NBS磨耗(%)

NBS abrasion

参数

parameter

50-65

6.0-8.0

350-450

≧15

15万次无裂口

150,000 times no crack

≧10

n   以上数据仅作参考,具体数据以实际操作为准。如需其他物性指标,请与我公司联系。

Datalisted above are just for reference.The detail data are subjected to practicaloperation.If other requests for Physical properties,please contact us.

n   该物性数据是对10mm厚的试片测试获得的

These physical data are acquired by testinga sample of 10mm thick.